l find that staggering because although the s&b brass is way better quality it is as thick as the PPU
have you measured the case head
because you are using light loads if it is over the size it should be l would suggest the cases heads are a bit soft from the manufacturer
this can be remedied by using a small base die, the brass will harden by firing it
the main thing is that you have found what works